Loctite LOCTITE 3D MED412 Resin - Ultra Clear - 1kg
LOCTITE 3D MED412 is a medical-grade 3D printing resin engineered for manufacturing Class I and II medical devices and equipment components. This high-impact material delivers exceptional elongation, durability, and surface finish while maintaining biocompatibility standards. Compatible with a broad range of DLP 3D printers, it's ideal for healthcare applications requiring stiffness and wear resistance.
- Meets ISO 10993-5, -10, and -23 biocompatibility standards with validated workflow.
- Superior elongation (105-115%) and high impact strength for durable medical components.
- Excellent surface finish and dimensional accuracy for professional medical applications.
LOCTITE MED412 RESIN
Medical Resins Designed for Durability
LOCTITE 3D MED412 medical-grade resin offers biocompatibility, meeting ISO 10993 standards with excellent impact strength and elongation for medical devices.
Key Features of the LOCTITE MED412 Resin:
- Compatible with a broad range of DLP 3D printers.
- Ideal for Class I and II medical devices and equipment components.
- Available in ultra clear and white color options.
Medical Grade Biocompatibility
LOCTITE 3D MED412 is designed to meet stringent ISO 10993-5, -10, and -23 biocompatibility standards when processed using validated workflows. This ensures safe use in medical device manufacturing and direct patient contact applications. Certificates of compliance are available upon request for regulatory submissions.
- ISO 10993 certified biocompatibility.
- Validated workflows for medical compliance.
- Certificates of compliance available.
High Impact Durability
Engineered for demanding medical applications, this resin delivers exceptional impact strength and superior elongation properties. The material maintains excellent mechanical performance after post-processing, making it ideal for components that require both flexibility and strength.
- IZOD impact strength of 47-52 J/m.
- Superior elongation at break (105-115%).
- Excellent stiffness and wear resistance.
Professional Surface Quality
MED412 produces parts with excellent surface finish and dimensional accuracy, reducing the need for extensive post-processing. The material is available in ultra-clear and white variants to meet different aesthetic and functional requirements for medical devices.
- Excellent surface finish quality.
- High-dimensional accuracy.
- Ultra clear and white color options.
TECHNICAL SPECIFICATIONS
- Cytotoxicity: Passed ISO 10993-5 standard, indicating non-cytotoxic properties.
- Irritation & Skin Sensitization: Successfully passed ISO 10993-10, ensuring minimal irritation and skin sensitization potential.
- Tests for Irritation: Passed ISO 10993-23 tests, indicating compliance with irritation standards.
- Elongation at Break: 141%
- Tensile Modulus: 1245 MPa
- Ultimate Tensile Strength: 38 MPa
- Impact Strength (Notched): 43 J/m
- Heat Deflection Temperature: 40°C
Note: Results conform to ISO and ASTM standards when utilizing an approved Henkel-validated workflow.
Workflow:
Validated workflows need to be followed to achieve properties as provided in the TDS. Examples of validated workflow steps are listed below. Users should defer to the most current workflow information for the best results which can be found here
Printer Settings:
LOCTITE 3D MED412 UCL is formulated to print optimally on industrial DLP printer. Read the safety data sheet carefully to get details about health and safety instructions. Recommended print parameters:
- Shake resin bottle well before usage
- Temperature: 20°C to 25°C
- Intensity: 4 mW/cm² to 8 mW/cm²
| Mechanical Properties | Measure Method | Green | Post Processed |
|---|---|---|---|
| Tensile Stress at Break (MPa) | ASTM D638 | 20 - 25 | 35 - 40 |
| Tensile Stress at Yield (MPa) | ASTM D638 | 28 - 23 | 30 - 38 |
| Young’s Modulus (MPa) | ASTM D638 | 850 - 1000 | 1250 - 1400 |
| Elongation at Break (%) | ASTM D638 | 115 - 130 | 105 - 115 |
| IZOD Impact (Notched) (J/m) | ASTM D256 | - | 47 - 52 |
| HDT at 0.455 MPa (°C) | ASTM D648 | - | 38 - 40 |
| HDT at 1.82 MPa (°C) | ASTM D648 | - | 34 - 35 |
| Shore Hardness (3s) (D) | ASTM 2240 | - | 70 |
| Water Absorption (24 hr) (%) | ASTM 570 | - | 0.27 – 0.28 |