Formlabs Formlabs High Temp Resin (1L) for Form 4
Formlabs High Temp Resin offers exceptional heat resistance with its highest achievable deflection temperature of 238°C, making it ideal for high-temperature applications such as molds and heat-resistant components. It facilitates the creation of durable, high-quality parts using resin 3D printing technology and is perfect for engineering and industrial uses requiring thermal stability.
- Heat deflection up to 238°C for thermal stability
- Formlabs' top material for high thermal resistance
- Ideal for molds, inserts, and heat-resistant components
- Cartridge compatible with Form 4 series 3D printers
| List Price: | $199.00 |
|---|---|
| Price: | $199.00 |
| Price: | $... |
High Temp Resin
ULTIMATE HEAT-RESISTANCE
Experience unparalleled thermal resilience with High Temp Resin, boasting the highest heat deflection temperature at 238°C for superior stability. Ideal for molds, inserts, and parts exposed to intense temperatures, it ensures precise, durable outcomes. Embrace easy experimentation with Formlabs' user-friendly technology. Perfect for heat-resistant mounts, housings, and fixtures, it's the ultimate choice for high-temperature applications.
Key Features of the Formlabs High Temp V2 Resin:
- Superior thermal stability for high-temperature applications
- Highest heat deflection temperature: 238°C @ 0.45 MPa
- Enables the creation of durable, high-quality end-use parts
- User-friendly experimentation with high-temperature projects
- Ideal for molds, inserts, and heat-resistant components
| Engineering Application |
SLA Technology |
Heat Resistant |
| 2.8 GPa Tensile Modulus |
230°C Heat Deflection Temp. @ 0.45 MPa |
49 MPa Ultimate Tensile Strength |
| COMPATIBILITY | ||
| Printer(s)* Form 4 / 4B Form 3L / 3BL Form 3+ / 3B+ Form 3 / 3B Form 2 |
Resin Tank(s) [RT] Form 4 / 4B RT Form 3L / 3BL RT V2 Form 3L / 3BL RT V1 Form 3 / 3B RT V2.1 Form 2 LT Tank Form 2 RT (PDMS) |
Build Platform(s) [BP] Form 4 BP Flex Form 4 BP Form 3L BP 2L Form 3L BP Form 3 Stainless Steel BP Form 3 BP 2 Form 3 BP |
*The resin is compatible with these 3D printers. Please ensure you're selecting the correct cartridge compatibility at purchase as the Form 4 uses a different cartridge system from previous models. The listing you are currently on is for the Form 4.
For the Form 3 series / Form 2 compatible cartridges, click here.
Why Choose High Temp Resins?
High Temp Resin stands as Formlabs' premier choice for heat stability, boasting the highest heat deflection temperature across our resin range.
- Unmatched Heat Resistance: Achieves the highest heat deflection temperature, ensuring superior thermal stability.
- User-Friendly: Designed for simplicity, allowing seamless experimentation with high-temperature projects.
High Temp Resin Applications
High Temp Resin, featuring the top Heat Deflection Temperature in Formlabs' lineup, is perfect for projects demanding exceptional heat resistance.
- Versatile Applications: Ideal for managing hot air, gas, and fluid flow.
- Durable Components: Creates heat-resistant mounts, housings, and fixtures.
- Precision Tooling: Suitable for producing molds and inserts.
What are the Material Properties of the Formlabs High Temp Resin?
| Green | Post-cured at 60ºC | |
| Tensile Modulus | 0.75 GPa | 2.8 GPa |
| Ultimate Tensile Strength | 21 MPa | 58 MPa |
| Elongation at Break | 0.14 | 0.033 |
| Flexural Modulus | 0.7 GPa | 2.6 GPa |
| Notched Izod | 33 J/m | 18 J/m |
Download the Formlabs High Temp Technical Data Sheet
Download the Formlabs High Temp Safety Data Sheet PDF
 |
 |
|---|---|
| FORM WASH SETTINGS | FORM CURE SETTINGS |
| Duration | Duration |
| 6 min | 120 min |
| Temperature | |
| 80°C | |
| Notes | Notes |
| Do not leave High Temp Resin in solvent for longer than 6 minutes total, as excessive solvent exposure affects the quality of the final part. |
There are several post-curing options for High Temp V2. Refer to the technical data sheet to understand how different options affect mechanical properties, and choose the post-cure option that is best suited to the intended application. To achieve the highest HDT of 238 °C @ 0.45 MPa: (1) Post-cure parts in Form Cure for 120 min at 80 °C. (2) Thermally post-cure parts in a non-food oven for 3 hours at 160 °C. For applications that do not require the maximum heat resistance, post-cure parts in Form Cure for 60 min at 60 °C. |